0Cr27Al7Mo2 is an iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1400°C (2552°F). The alloy with the characteristics of high resistivity, low temperature coefficient of electric resistance, high operating temperature, good oxidation resistance under high temperature. It can equal to APM.
- Melting Furnace Heating Elements
Industrial melting furnaces typically require high temperatures to melt metals or other materials. 0Cr27Al7Mo2 resistance wire is used as heating elements in melting furnaces, capable of operating stably at extremely high temperatures, providing the required heating power to ensure smooth melting processes.
- Heat Treatment Furnace Heaters
Heat treatment is an important process in the metalworking industry, used to improve the physical and chemical properties of metals. 0Cr27Al7Mo2 resistance wire is used as heating elements in heat treatment furnaces, providing high-temperature heating to bring metals to the required treatment temperature, meeting the requirements of heat treatment processes.
- Glass Processing Furnace Heaters
In the glass manufacturing industry, glass processing furnaces are used to heat glass raw materials and melt them to produce various glass products. 0Cr27Al7Mo2 resistance wire is used as heating elements in glass processing furnaces, providing stable heating power in high-temperature environments, ensuring uniform heating of glass raw materials and achieving high-quality glass manufacturing.
- Chemical Reaction Vessel Heaters
Many chemical reactions in the chemical industry need to be carried out at specific temperatures. 0Cr27Al7Mo2 resistance wire is used as heating elements in chemical reaction vessels, providing reliable heating effects to ensure that chemical reactions occur within the required temperature range, achieving reaction control and optimization.
- Industrial Baking Oven Heaters
In industries such as food processing and paint curing, baking ovens are commonly used for heating and drying. 0Cr27Al7Mo2 resistance wire is used as heating elements in industrial baking ovens, providing appropriate heating power to ensure that products receive good heating effects during the baking process.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | | Nb0.5 | Mo1.8-2.2 |
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |